Evolution of carbon nanostructure during pyrolysis of homogeneous chitosan-cellulose composite fibers

Abstract : Chitosan-cellulose composite fibers spun using a Lyocell technology are characterized by a homogeneous distribution and a close packing of the two biopolymers inside the fibrous matrix. Due to the intimate contact of cellulose and chitosan, synergistic effects can be observed during the pyrolysis of the composite fibers. In this study, the catalytic role of chitosan in altering the cellulose pyrolysis pathway in the composite fibers at moderate treatment temperatures up to 900 C is confirmed. Analyses of the evolved gases during pyrolysis revealed that chitosan promoted cellulose dehydration and substantially decreased the formation of levoglucosan, explaining the higher char yield. The enhanced dehydration reaction is associated with the formation of intermolecular crosslinks due to the incorporation of nitrogen from chitosan in the resulting carbon structures. Nitrogen could also contribute to the in-plane disorder in the aromatic clusters when the pyrolysis is carried out at 500e700 C, although the inplane disorder is less noticeable from 700 to 900 C. Nevertheless, the size of the aromatic cluster continues to grow when the composite fibers are pyrolyzed in a temperature range of 500e900 C.
Document type :
Journal articles
Complete list of metadata

https://hal.archives-ouvertes.fr/hal-03431827
Contributor : Yu Ogawa Connect in order to contact the contributor
Submitted on : Tuesday, November 16, 2021 - 10:49:51 PM
Last modification on : Friday, April 1, 2022 - 3:47:32 AM
Long-term archiving on: : Thursday, February 17, 2022 - 9:30:30 PM

File

1-s2.0-S000862232100854X-main ...
Publisher files allowed on an open archive

Identifiers

Collections

Citation

Hilda Zahra, Daisuke Sawada, Shogo Kumagai, Yu Ogawa, Leena-Sisko Johansson, et al.. Evolution of carbon nanostructure during pyrolysis of homogeneous chitosan-cellulose composite fibers. Carbon, 2021, 185, pp.27 - 38. ⟨10.1016/j.carbon.2021.08.062⟩. ⟨hal-03431827⟩

Share

Metrics

Record views

18

Files downloads

23